Poligraph 140 LV Plus Premium Resin

• Fast curing cycle.

   

• Fully compatible with pigments.

   

• High mechanical properties.

   

• Improves thermal conductivity.

• Designed as a base resin for working with fibreglass or injection resins.

   

• Good interlayer adhesion and very low linear and volumetric shrinkage.

   

• Inert mineral fillers such as calcium carbonates, calcium sulphates, dolomite, or silicas can be added. The percentage of MEKP (Methyl Ethyl Ketone Peroxide) to be added ranges between 0.75% and 1%, although it can be increased up to 2% to reduce gel time.

   

• The application can be manual or by machine.

   

• May be used in pultrusion processes.

• The product must be stored in a dry place at a temperature not exceeding 25ºC.
• Its expiry date is 4 months under these conditions.
• Generally, products will be supplied in drum format.
• For other quantities, please contact us.

• Appearance: Dark liquid

   

• Peak exothermic temperature (in 45 min): 95 ºC

   

• Density: 1.54 g/cm³

   

• Gel time (25ºC) (100/0.3 CO/0.6 PMEK): 10 – 15 min

   

• Brookfield viscosity (H2V30, 25ºC): 400 – 800 cps

• Flexural modulus: 8,300 – 10,200 MPa
• Flexural strength: 40 – 60 MPa
• Maximum deflection: 0.4 – 0.6 mm
• Tensile modulus: 5,000 – 6,000 MPa
• Tensile strength: 25 – 45 MPa
• Elongation at break: 0.5 – 0.7 %

Mechanical properties of the catalysed resin